Method of producing nano- and microcapsules of spider silk protein

ABSTRACT

The present invention is directed to a method of producing nano- and microcapsules from spider silk proteins The invention is further directed to nano- or microcapsules obtainable by this method as well as pharmaceutical, cosmetical and food compositions containing same.

This application is a divisonal application of U.S. application Ser. No. 11/989,907, filed Nov. 13, 2009, which is a 371 national stage patent application of international patent application no. PCT/EP2006/007608 filed Aug. 1, 2006, which claims priority to European patent application no. 05016712.1, filed Aug. 1, 2005, all of which are incorporated herein by reference in their entireties for all purposes.

The present invention is directed to a method of producing nano- and microcapsules from spider silk proteins. The invention is further directed to nano- or microcapsules obtainable by this method as well as pharmaceutical, cosmetical and food compositions containing same.

Small-scale structures are of great interest as transport vesicles and as potential building blocks for future devices. One task is to be able to encapsulate reactants or particles at small scales and to allow triggered release of the encapsulated matter after placing them at a specific location. One solution for such problem is the use of chemical vesicles, so called nano-capsules. The nano-capsules are designed to set the reactants free upon an external trigger or stimulus. Several problems arise from such quest: the most important one is how to build such nano-capsules in a defined way around e.g. chemically or biologically active reactants.

Recently, “hybrid” stimuli-responsive nano-capsules have been developed to fulfill such needs. The structures (vesicles but also micelles) are obtained from the self-assembly of e.g. ampihiphile polybutadiene (PB)-b-poly(glutamic acid) (PGA) diblock copolymers, which have a pH-sensitive conformation. The pH-sensitivity can be used to unload the vesicles. Those PB-b-PGA copolymers bearing a cross-linkable hydrophobic block and a hydrophilic peptidic block have been synthesized by combining anionic and ring-opening polymerization (Chécot et al., 2002). The polydispersity of the copolymers is small enough to obtain well defined self-assembled aggregates. For example a PB40-b-PGA100 copolymer when in water forms closed bilayer vesicles called polymersomes (Won et al., 1999). One property of the vesicles is that they respond to an external pH shift by changing in size (FIG. 1). This transition upon pH changes is reversible and only moderately sensitive to salinity, since it is not based on a simple polyelectrolyte swelling effect, but on the peptidic nature of the PGA block (FIG. 1). These vesicles are not only able to encapsulate low molecular weight compounds (like solvent molecules such as fluorophors (Chécot et al., 2003)), but can also stabilize larger nanoparticles. The disadvantage of such systems is the partial incompatibility with biological systems, which usually are highly sensitive to dramatic pH changes, since pH changes can result in a loss in biological activity of the encapsulated sample.

FIG. 1 for illustration shows (a) Dynamic Light Scattering of the peptosome's hydrodynamic radius R_(H) as a function of NaCl concentration and pH. (b) Schematic representation of the peptosome and its change in size as function of pH due to a coil to α-helix secondary structure transition in the peptide part.

Another established encapsulation method is the self-assembly of colloidal particles at the oil/water interphase. The driving force for the self-assembly process is the minimization of the total surface energy—thus a wide variety of particles and solvents can be used. Such stabilized emulsions are well known as Pickering emulsions. The stabilization or crosslinking of the particles leads to mechanical stable cages, which can than be transferred to the continuous phase. The advantages of the so called colloidosomes are the control of the encapsulate and the ease of tuning the mechanical and chemical stability of the outer shell. The self-assembly of the particles results in an almost crystalline structure and thus holes between the particles will occur. These holes are a size selective filter which allows the control of the diffusion across the membrane (Dinsmore et al., 2000). The whole process can be performed in a biocompatible way. However, the colloidal particles themselves are not necessarily biocompatible.

WO 02/47665 describes a method for making self-assembled, selectively permeable elastic microscopic structures, referred to as colloidosomes, that have controlled pore-size, porosity and advantageous mechanical properties. The method comprises: (a) providing particles formed from a biocompatible material in a first solvent; (b) forming an emulsion by adding a first fluid to said first solvent, said emulsion being defined by droplets of said first fluid surrounded by said first solvent; (c) coating the surface of said droplets with said particles; and (d) stabilizing said particles on said surface of said droplet to form colloidosomes having a yield strength of at least about 20 Pascals. WO 02/47665 uses biocompatible synthetic polymers for producing these colloidosomes. Examples are polystyrene, polymethylmethacrylate, polyalkylenes, silica and combinations thereof The particles from which the colloidosomes are to be obtained are stabilized for example by sintering, chemical crosslinking and the like. However, the method of preparing those colloidosomes is comparably difficult and the colloidal particles used may show harmful properties for in vivo applications due to their artificial and non natural nature. By using colloidal particles limits also the size range of the shells, since using colloids limits the minimal size bag with defined holes.

Therefore, it is a problem underlying the present invention to provide nano-and microcapsules, which are highly biocompatible and thus suitable for in vivo applications. It is another problem of this invention to obtain nano- and microcapsules, which are capable to accommodate different types and varying amounts of effective agents or nutritions etc. A further problem underlying the present invention is to provide nano- and microcapsules which are biodegradable, i.e. which are capable of a controlled release of said effective agents etc. in vivo, for example in topical or systemic applications.

These problems are solved by the subject-matter of the independent claims. Preferred embodiments are set forth in the dependent claims.

In the present invention, it surprisingly turned out that spider silk proteins may serve as a base for forming micro- and nanocapsules which can be used for various in vivo applications. It in particular turned out that this can be done by an improved method of producing said capsules, which does circumvent the need of using steps to link or stabilize the particles from which the capsules are formed by addition of chemicals like crosslinkers or which requires sintering or the like which could have deleterious effects on the agents to be packaged into said micro- and nanocapsules.

Since most currently used encapsulation techniques (see for example WO 02/47665) rely on non-biological particles or macromolecules, the inventors developed a new stable encapsulation process based on self-assembling spider silk proteins. Unlike other encapsulation technologies, in the present method the hydrophobic/hydrophilic nature of the emulsion surface is not only used to assemble colloid particles, but it is also used as the driving force for the colloid immobilization through coalescence and polymer network formation (stabilization). This process represents not only a method to produce polymeric nano- and microcapsules formed from a new class of biocompatible colloids, it also represents a novel approach to polymer network formation using proteins. The big advantage of nano- and microcapsules formed from this method is the biocompatibility and the functionality of the microcapsules imparted by the proteins. This enables the control of the release mechanisms by several means: pH changes, temperature changes, or activity of proteases.

For example, the nano- or microcapsules might be destroyed and their ingredients might be released in vivo chemically, physically (for example by shear forces) or biologically (by proteolytic digestion).

The self-assembly of the spider silk proteins at the interface was achieved by introducing the protein into the water phase of a water/oil emulsion (see FIG. 2). The minimization of surface energy was driving the proteins to the interface and induced an aggregation of the monomers to a dense polymer network (FIG. 3).

The spider bags/balloons formed from this process are for example filled with the contents of the water phase and can exist in organic solvents, alcohols as well as in water (FIG. 3). Therefore, they are showing an unexpected stability in strongly differing environments. In principal the self-assembly of proteins at an inverse emulsion surface is also possible-thus encapsulating the content of the oil phase (see also below).

Strikingly, the bags/balloons can be filled with proteins, chemical reactants, nano- and micrometer scaled particles, etc., which is exemplarily shown by filling the particles with fluorescently (FITC)-labeled Dextran particles (FIG. 4).

The impermeability of the membrane and the mechanical stability of the bags against osmotic stresses are both relatively high, considering the thickness of the membrane. Electron microscopy images reveal that the thickness is between 10 and 70 nm (FIG. 5).

In the present approach synthetic spider silk proteins have been employed, in particular the synthetic sequence of C₁₆ (Huemmerich et al., 2004) to create a biological encapsulation of active agents.

Spider silks in general are protein polymers that display extraordinary physical properties, but there is only limited information on the composition of the various silks produced by different spiders (see Scheibel, 2004). Among the different types of spider silks, draglines from the golden orb weaver Nephila clavipes and the garden cross spider Araneus diadematus are most intensely studied. Dragline silks are generally composed of two major proteins and it remains unclear whether additional proteins play a significant role in silk assembly and the final silk structure. The two major protein components of draglines from Araneus diadematus are ADF-3 and ADF-4 (Araneus Diadematus Fibroin).

Genes coding for spider silk-like proteins were generated using a cloning strategy, which was based on a combination of synthetic DNA modules and PCR-amplified authentic gene sequences (Huemmerich et al., 2004). The dragline silk proteins ADF-3 and ADF-4 from the garden spider Araneus diadematus were chosen as templates for the synthetic constructs. A seamless cloning strategy allowed controlled combination of different synthetic DNA modules as well as authentic gene fragments. A cloning vector was designed comprising a cloning cassette with a spacer acting as placeholder for synthetic genes (Huemmerich et al., 2004).

To mimic the repetitive sequence of ADF-4 a single conserved repeat unit has been designed to gain one consensus module termed C, which was multimerized to obtain the repetitive protein C₁₆, which was employed in the given approach as an example.

There are many possible applications for the presented spider silk bags/balloons, ranging from functional food to pharmaceutical to cosmetical applications. For example the encapsulation in food technology could protect certain ingredients such as vitamins from an oxidizing environment. In another food technology application, ingredients such as fish oil could be hidden from taste. In pharmaceutical applications the diffusion barrier of the protein shell allows for slow (controlled) release processes for the encapsulated material. The further design of the protein shells could result in a defined release container, which liberates the content only after activation using certain proteases or other triggers. In cosmetics the transport of water active ingredients into the skin could be facilitated by the presented bags/balloons, after slow degradation of the protein shell, e.g. by proteases of the skin. Further, mechanical shearing can be used to liberate the content upon exposure to the skin.

The present invention in particular is directed to the following aspects and embodiments:

According to a first aspect, the present invention is directed to a method of producing nano- and microcapsules comprising the steps of:

-   a) providing spider silk proteins; -   b) forming a solution or suspension of said proteins in a suitable     solvent; -   c) generating an emulsion of at least two phases, said emulsion     containing the solution or suspension formed in b) as a first phase     and at least one further phase, which is substantially immiscible     with said first phase; -   d) forming a polymer network of the spider silk proteins at the     interface of the at least two phases; -   e) separating the protein polymer network generated in (d) from the     emulsion.

As explained above, it unexpectedly turned out that forming the polymer network in step d) does not require the addition of any further ingredients (for example crosslinkers) and there is no need for additional steps as sintering, crosslinking etc.

It is noted that the term “spider silk protein” as used herein does not only comprise all natural sequences but also all artificial or synthetic sequences which were derived therefrom.

Accordingly, the spider silk sequences may be derived from sequences which are termed “authentic” herein. This term means that the underlying nucleic acid sequences are isolated from their natural environment without performing substantial amendments in the sequence itself The only modification, which is accepted to occur, is where the authentic nucleic acid sequence is modified in order to adapt said sequence to the expression in a host without changing the encoded amino acid sequence. Preferred sequences are NR3 (SEQ ID NO: 10; derived from ADF-3) and NR4 (SEQ ID NO: 11; derived from ADF-4). In both sequences, for more efficient translation, the codon AGA (Arg), which is rarely translated in E. coli, was mutated to CGT (Arg) using PCR mutagenesis.

The authentic non-repetitive sequences are preferably derived from the amino terminal non-repetitive region (flagelliform proteins) and/or the carboxy terminal non-repetitive region (flagelliform and dragline proteins) of a naturally occurring spider silk protein. Preferred examples of those proteins will be indicated below.

According to a further embodiment, the authentic non-repetitive sequences are derived from the amino terminal non-repetitive region (flagelliform proteins) and/or the carboxy terminal non-repetitive region (flagelliform and dragline proteins) of a naturally occurring spider silk protein.

Preferred authentic sequences of flagelliform proteins are the amino acid sequence and nucleic acid sequence of FlagN-NR (SEQ ID NOs: 31 and 32) and FlagC-NR (SEQ ID NOs: 33 and 34).

The recombinant spider silk proteins of the invention generally may be derived from spider dragline proteins from the spider's major ampullate gland and/or from proteins derived from the flagelliform gland.

According to an embodiment, the recombinant (synthetic/artificial) spider silk proteins which can be used in the present invention generally are derived from spider dragline proteins from the spider's major ampullate gland and/or from proteins derived from the flagelliform gland.

It is generally preferred to select the dragline and/or flagelliform sequences from dragline or flagelliform proteins of orb-web spiders (Araneidae and Araneoids).

More preferably the dragline proteins and/or flagelliform proteins are derived from one or more of the following spiders: Arachnura higginsi, Araneus circulissparsus, Araneus diadematus, Argiope picta, Banded Garden Spider (Argiope trifasciata), Batik Golden Web Spider (Nephila antipodiana), Beccari's Tent Spider (Cyrtophora beccarii), Bird-dropping Spider (Celaenia excavata), Black-and-White Spiny Spider (Gasteracantha kuhlii), Black-and-yellow Garden Spider (Argiope aurantia), Bolas Spider (Ordgarius furcatus), Bolas Spiders-Magnificent Spider (Ordgarius magnificus), Brown Sailor Spider (Neoscona nautica), Brown-Legged Spider (Neoscona rufofemorata), Capped Black-Headed Spider (Zygiella calyptrata), Common Garden Spider (Parawixia dehaani), Common Orb Weaver (Neoscona oxancensis), Crab-like Spiny Orb Weaver (Gasteracantha cancriformis (elipsoides)), Curved Spiny Spider (Gasteracantha arcuata), Cyrtophora moluccensis, Cyrtophora parnasia, Dolophones conifera, Dolophones turrigera, Doria's Spiny Spider (Gasteracantha doriae), Double-Spotted Spiny Spider (Gasteracantha mammosa), Double-Tailed Tent Spider (Cyrtophora exanthematica), Aculeperia ceropegia, Eriophora pustulosa, Flat Anepsion (Anepsion depressium), Four-spined Jewel Spider (Gasteracantha quadrispinosa), Garden Orb Web Spider (Eriophora transmarina), Giant Lichen Orbweaver (Araneus bicentenarius), Golden Web Spider (Nephila maculata), Hasselt's Spiny Spider (Gasteracantha hasseltii), Tegenaria atrica, Heurodes turrita, Island Cyclosa Spider (Cyclosa insulania), Jewel or Spiny Spider (Astracantha minax), Kidney Garden Spider (Araneus mitificus), Laglaise's Garden Spider (Enrovixia laglaisei), Long-Bellied Cyclosa Spider (Cyclosa bifida), Malabar Spider (Nephilengys malabarensis), Multi-Coloured St Andrew's Cross Spider (Argiope versicolor), Ornamental Tree-Trunk Spider (Herennia ornatissima), Oval St. Andrew's Cross Spider (Argiope aemula), Red Tent Spider (Cyrtophora unicolor), Russian Tent Spider (Cyrtophora hirta), Saint Andrew's Cross Spider (Argiope keyserlingi), Scarlet Acusilas (Acusilas coccineus), Silver Argiope (Argiope argentata), Spinybacked Orbweaver (Gasteracantha cancriformis), Spotted Orbweaver (Neoscona domiciliorum), St. Andrews Cross (Argiope aetheria), St. Andrew's Cross Spider (Argiope Keyserlingi), Tree-Stump Spider (Poltys illepidus), Triangular Spider (Arkys clavatus), Triangular Spider (Arkys lancearius), Two-spined Spider (Poecilopachys australasia), Nephila species, e.g. Nephila clavipes, Nephila senegalensis, Nephila madagascariensis and many more (for further spider species, see also below). Most preferred, the dragline proteins are derived from Araneus diadematus and the flagelliform proteins are derived from Nephila clavipes.

In the context of this invention, it should be clear that a recombinant spider silk protein may not only comprise protein sequences from one species, but may also contain sequences derived from different spider species. As an example, the one or more synthetic repetitive spider silk protein sequences might be derived from one species, the one or more authentic non-repetitive spider silk protein sequences from another. As a further example, it is also possible to design a recombinant spider silk protein, which contains more than one type of a repetitive sequence, wherein the different types are derived from different species.

According to one preferred embodiment, the dragline protein is wild type ADF-3, ADF-4, MaSp I, MaSp II and the flagelliform protein is FLAG. The term ADF-3/-4 is used in the context of MaSp proteins produced by Araneus diadematus (Araneus diadematus fibroin-3/-4). Both proteins, ADF-3 and -4 belong to the class of MaSp II proteins (major ampullate spidroin II).

In a further embodiment, the nucleic acid sequence provided is ADF-3 (SEQ ID NO:1) and/or ADF-4 (SEQ ID NO: 2), or a variant thereof.

It is noted that two different kinds of ADF-3 and ADF-4 coding sequences and proteins are contemplated in this invention: first, the already published sequence of ADF-3 and ADF-4 (herein: “wild type” sequence) and, second, a variant thereof, encoded by SEQ ID NO: 1 (ADF-3) and 2 (ADF-4). The wild type sequences were already published and are available under the accession numbers U47855 and U47856 (SEQ ID NO: 8 and 9).

Further spider silk proteins, which can be used in this invention (i.e. alone or in combination with further proteins) and their database accession numbers are:

-   spidroin 2 [Araneus bicentenarius]gi|2911272 -   major ampullate gland dragline silk protein-1 [Araneus ventricosus]     gi|27228957 -   major ampullate gland dragline silk protein-2 [Araneus     ventricosus]gi|27228959 ampullate spidroin 1 -   [Nephila madagascariensis]gi|13562006 -   major ampullate spidroin 1[Nephila senegalensis]gi|13562010 -   major ampullate spidroin 1 [Latrodectus geometricus]gi|13561998 -   major ampullate spidroin 1 [Argiope trifasciata]gi|13561984 -   major ampullate spidroin 1 [Argiope aurantia]gi|13561976 -   dragline silk protein spidroin 2 [Nephila clavata]gi|16974791 -   major ampullate spidroin 2 [Nephila senegalensis]gi|13562012 -   major ampullate spidroin 2 [Nephila madagascariensis]gi|13562008 -   major ampullate spidroin 2 [Latrodectus geometricus]gi|13562002

According to another preferred embodiment, the flagelliform protein is SEQ ID NO: 6 (Flag-N) and/or SEQ ID NO: 7 (Flag-C) or a variant thereof.

However, also already known and published flagelliform sequences may be used herein, in particular the following:

-   Flagelliform silk protein partial cds [Nephila clavipes]gi|2833646 -   Flagelliform silk protein partial cds [Nephila clavipes]gi|2833648

In one preferred embodiment, the recombinant spider silk protein comprises one or more synthetic repetitive sequences containing one or more polyalanine containing consensus sequences. Those polyalanine sequences may contain from 6 to 9 alanine residues. See, for example SEQ ID NO: 1, containing several polyalanine motifs of 6 alanine residues.

Preferably, the polyalanine containing consensus sequence is derived from ADF-3 and has the amino acid sequence of SEQ ID NO: 3 (module A) or a variant thereof. Module A contains a polyalanine having 6 alanine residues. A further preferred polyalanine containing consensus sequence, derived from ADF-4, is module C (SEQ ID NO: 5), containing 8 alanine residues.

According to a further preferred embodiment, in the recombinant spider silk protein of the invention, the synthetic repetitive sequence is derived from ADF-3 and comprises one or more repeats of the amino acid sequence of SEQ ID NO: 4 (module Q) or a variant thereof.

In more general words, a synthetic repetitive sequence may also contain the general motifs: GGX or GPGXX, i.e. glycine rich regions. As mentioned above, these regions will provide flexibility to the protein and thus, to the thread formed from the recombinant spider silk protein containing said motifs.

It is noted that the specific modules for the synthetic repetitive sequence for use in the present invention can also be combined with each other, i.e. modules (repeat units) combining A and Q, Q and C etc. are also encompassed by the present invention. Although the number of the modules to be introduced in the spider silk protein is not restricted, it is preferred to employ a number of modules of the synthetic repetitive sequence for each recombinant protein which number is preferably ranging from 5-50 modules, more preferably 10-40 and most preferably between 15-35 modules.

The synthetic repetitive sequence preferably comprises one or more of (AQ) and/or (QAQ) as repeat units. Even more preferred, the synthetic repetitive sequence is (AQ)₁₂, (AQ)₂₄, (QAQ)₈ or (QAQ)₁₆.

Whenever the synthetic repetitive sequence is derived from ADF-4, it may preferably comprise one or more repeats of the amino acid sequence of SEQ ID NO: 5 (module C) or a variant thereof, as mentioned above, wherein the overall synthetic repetitive sequence is C₁₆ or C₃₂.

Preferred embodiments for the complete recombinant spider silk proteins of the invention are (QAQ)₈NR3, (QAQ)₁₆NR3, (AQ)₁₂NR3, (AQ)₂₄NR3, C₁₆NR4 and C₃₂NR4 i.e. proteins which comprise or consist of said sequences.

It is noted that the above configuration of the synthetic repetitive sequence (using the A, Q and C system) also applies to all other repeat units disclosed above, for example all polyalanine containing sequences can be taken for A and/or C and all glycine rich sequences may be used as Q.

New modules for synthetic repetitive sequences derived from flagelliform sequences are modules K (SEQ ID NO: 35 and 36), sp (SEQ ID NO: 37 and 38), X (SEQ ID NO: 39 and 40), and Y (SEQ ID NO: 41 and 42):

The synthetic repetitive sequence also preferably comprises or consists of Y₈, Y₁₆, X₈, X₁₆, K₈, K₁₆. Furthermore, it is also possible, to combine those sequences derived from ADF-3 and ADF-4 and Flag in one recombinant sequence.

In the present invention it is however strongly preferred to employ spider silk proteins in step a) which are selected from or containing sequences of the group of ADF-4 sequences and derivatives thereof including C₁₆, C₁₆NR4, C₃₂ and/or C₃₂NR4.

In the present invention the spider silk proteins can be further engineered to contain single amino acid substitutions or direct chemical modifications before capsule production, or the latter also after capsule production. This can be used to introduce e.g. specific binding affinities to the bags or to introduce protease specific amino acid sequences. This may result in a controlled release of the encapsulate by proteolytic digestion of the silk membrane.

By introducing e.g. single cysteines crosslinking of the bag or the covalent coupling of different functional groups can be achieved. For example, replacing nucleic acids encoding one or more amino acids in a spider silk protein by a lysine or cysteine encoding nucleic acid sequence, and/or adding a nucleic acid sequence containing nucleic acids encoding lysine and/or cysteine to said sequence, may achieve this.

Further, agents may be coupled to the spider silk proteins before and after formation of the nano- or microcapsules in order to direct the capsules to specific cells or tissues. This can be achieved, for example, by introducing or covalent coupling of specific RGD sequences. Thus, RGD peptides may be cross-linked to the spider silk proteins before and after formation of the nano- or microcapsules. Examples for cyclic RGD molecules are indicated in FIG. 10.

Furthermore, cell or tissue specific antibodies and cell or tissue specific receptors might be coupled to the spider silk proteins to direct the capsules to a specific target.

According to a further embodiment, the solvent in b) and/or the solvents of the at least one further phase is selected from the group consisting of hydrophilic solvents, preferably water, alcohols like ethanol, glycerol, or lipophilic solvents, preferably natural oils, such as oils of plant or animal origin, synthetic oils, such as miglyol, silicon oil, organic solvents, such as aromatic hydrocarbons, for example toluene, benzene etc.

It is noted that one single phase may contain also more than one solvent (i.e. a mixture) as long as the solvents are substantially identical. “Substantially identical” means that the solvents are having similar solubility properties thus forming only one common phase. Thus, “substantially identical” solvents include solvents in which one can not observe separate phases if the solvents are blended. As an example, two or more lipophilic solvents may be combined into one phase, for example a plant oil (for example olive oil and castor oil) and miglyol and/or hexadecane. Or, as an alternative, a hydrophilic phase may comprise two or more hydrophilic components, for example water, glycerol and the like.

As mentioned above, the only requirement is that the emulsion system for producing the nano- and microcapsules of the invention has at least two phases, wherein the phases are substantially immiscible.

All known emulsion types may be employed in step c) of the present method, for example W/O, O/W, O/W/O or W/O/W type emulsions. These emulsion types are well known in the art and for further information it is for example referred to “Remington's Pharmaceutical Sciences”, Mack Publishing Co., Easton, Pa., latest edition or further available information.

A preferred method for forming the emulsions of the present invention is to produce a mini-emulsion. Mini-emulsions are dispersions of critically stabilized oil droplets with a size between 50 and 500 nm prepared by shearing a system containing oil, water, a surfactant and a hydrophobic agent. Polymerizations in such mini-emulsions, when carefully prepared, result in particles which have about the same size as the initial droplets. This means that the appropriate formulation of a mini-emulsion suppresses coalescence of droplets or Ostwald ripening. The preparation of the mini-emulsion is done by high shear devices such as ultrasound and high-pressure homogenizers. It is referred to the various publications of K. Landfester and coworkers.

In case of an emulsion of the W/O type, the W (hydrophilic) phase is forming the emulsion droplets and in this case, the spider silk proteins are contained in the W phase. The O phase is the lipophilic phase and forms the continuous phase.

In case of an emulsion of the O/W type, the O (lipophilic) phase is forming the emulsion droplets and in this case, the spider silk proteins are contained in the O phase. The W phase is the hydrophilic phase and forms the continuous phase.

The surfactants used in the above emulsions may be selected from those compounds, the skilled person will use based on the available knowledge in the field of pharmaceutical and related sciences. An exemplary selection of surfactants for use in obtaining the present emulsions are fatty acid esters of glycerols, sorbitol and other multifunctional alcohols, preferably, glycerol monostearate, sorbitan monolaurate, or sorbitan monoleate; poloxamines; polyoxyethylene ethers and polyoxyethylene esters; ethoxylated triglycerides; ethoxylated phenols and ethoxylated diphenols; metal salts of fatty acids, metal salts of fatty alcohol sulfates, sodium lauryl sulfate; and metal salts of sulfosuccinates: polysorbates, more preferably polysorbate 20, 40, 60 and 80: poloxamers, polyoxyethylene glycols; and mixtures of said substances.

However, it is explicitly noted that it is not an essential feature of this invention to use a surfactant. The skilled artisan is aware of emulsion systems, which do not require surfactants.

In a preferred embodiment of the present invention, the solvent used in 1b) further contains one or more pharmaceutical agents, cosmetical agents, foodstuffs or food additives. In other words, the additional ingredients usually will be present in the phase, which is also containing the spider silk proteins. In this case, the one or more ingredients/agents will be encapsulated into the polymer network which is formed at the phase-interface.

As an alternative, it is also possible to add the above mentioned agents to the continuous phase, which does not contain the spider silk proteins. In this case, the nano- and microcapsules of the invention will be coated by said agents.

As a further alternative, the agents may be introduced into the nano- and microcapsules of the invention after they have been obtained by the present method.

This can be done by swelling the membrane with certain solvents and letting the encapsulate (effective agent) diffuse inside. Swelling could also be done by temperature, pressure or not only solvents but also other chemical means (such as chemical agents, pH, and others).

It is also possible to incorporate the encapsulate into the membrane. This approach may give amended or improved release properties than encapsulating the encapsulate into it.

The type of agent which is additionally incorporated into the nano- and microcapsules of the invention is not restricted in any way.

For example, the pharmaceutical agent may be selected from the group consisting of analgesics; hypnotics and sedatives; drugs for the treatment of psychiatric disorders such as depression and schizophrenia; anti-epileptics and anticonvulsants; drugs for the treatment of Parkinson's and Huntington's disease, aging and Alzheimer's disease; drugs aimed at the treatment of CNS trauma or stroke; drugs for the treatment of addiction and drug abuse; chemotherapeutic agents for parasitic infections and diseases caused by microbes; immunosuppressive agents and anti-cancer drugs; hormones and hormone antagonists; antagonists for non-metallic toxic agents; cytostatic agents for the treatment of cancer; diagnostic substances for use in medicine; immunoactive and immunoreactive agents; antibiotics; antispasmodics; antihistamines; antinauseants; relaxants; stimulants; cerebral dilators; psychotropics; vascular dilators and constrictors; anti-hypertensives; drugs for migraine treatment; hypnotics, hyperglycemic and hypoglycemic agents; anti-asthmatics; antiviral agents; and mixtures thereof

Foodstuffs and food additives may be selected from the group consisting of vitamines (ascorbic acid, tocopherol acetate and the like), minerals (calcium, magnesium, potassium, sodium, for example), trace elements (selenium), extracts of natural origin, natural oils (fish oil) etc.

Cosmetical agents may be selected for example from tocopherol acetate, oils of natural or synthetic origin, panthenol, plant extracts, UV absorbing agents, desinfectants, anti-irritant agents, repellants.

It is noted that the agents might be present in the solvent in dissolved, suspended or solid form. In the latter case, a solid core is provided which is coated by the spider silk proteins of the present invention.

In a preferred embodiment, the separation of the polymer network in step e) is done by means of centrifugation or by destroying the emulsion formed in step c) and forming a one-phase solution. However, also other methods may be used in order to separate the nano- and microcapsules of the present invention from the emulsion system.

The temperature used in steps b)-e) is 5-40° C., preferably 10-30 and more preferably room temperature. The pH used in steps b)-e) is 3-9, preferably 5-8, more preferably 7.

The size of the emulsion droplets and the nano- and microparticles derived therefrom is preferably from 10 nm to 40 μm, preferably between 500 nm and 10 μm, most preferably about 5 μm. The wall thickness of the obtained nano- and microcapsules preferably is between 5 and 100 nm, more preferably between 10 and 70 nm (see for example FIG. 5).

In a second aspect, the present invention provides nano- and microcapsules obtainable by the method as disclosed above.

A third aspect of the present invention is directed to a pharmaceutical composition containing nano- and microcapsules as defined above and one or more pharmaceutically acceptable carriers. Thus, the active components of the present invention are preferably used in such a pharmaceutical composition in doses mixed with an acceptable carrier or carrier material, that the disease can be treated or at least alleviated. Such a composition can (in addition to the active component and the carrier) include filling material, salts, buffer, stabilizers, solubilizers and other materials, which are known state of the art.

The term “pharmaceutically acceptable” is defined as non-toxic material, which does not interfere with effectiveness of the biological activity of the active component. The choice of the carrier is dependent on the application.

The pharmaceutical composition can contain additional components which enhance the activity of the active component or which supplement the treatment. Such additional components and/or factors can be part of the pharmaceutical composition to achieve a synergistic effects or to minimize adverse or unwanted effects.

Techniques for the formulation or preparation and application/medication of compounds of the present invention are published in “Remington's Pharmaceutical Sciences”, Mack Publishing Co., Easton, Pa., latest edition (see also above). An appropriate application can include for example oral, dermal or transmucosal application and parenteral application, including intramuscular, subcutaneous, intramedular injections as well as intrathecal, direct intraventricular, intravenous, intraperitoneal or intranasal injections.

In a fourth aspect, the present invention provides a cosmetical or food product containing nano- and microcapsules as disclosed hereinabove.

All publications, patent applications, patents, and other references mentioned herein are incorporated by reference in their entirety. In case of conflict, the present specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.

The invention is now further illustrated by the accompanying figures, in which:

FIG. 1 shows (a) Dynamic Light Scattering of the peptosome's hydrodynamic radius R_(H), as a function of NaCl concentration and pH. (b) Schematic representation of the peptosome and its change in size as function of pH due to a coil to a-helix secondary structure transition in the peptide part.

FIG. 2 is an schematic illustration of the spider bag/balloon formation process. (A) An aqueous protein suspension is emulsified in toluene. (B) Protein adsorbs at the water-toluene interface and denatures forming a polymer network (Inset). (C) Once adsorbed, the protein network can be transferred into water by centrifugation. The final bag/balloon structures have water on the inside and water on the outside. (D) Alternatively, once adsorbed, the protein network can be transferred into a one-phase solution through the addition of ethanol.

FIG. 3 shows an image of spider bags/balloons in (A) toluene/ethanol (50:50) and (B) after transfer into water.

FIG. 4 is an image of spider bags/balloons filled with FITC-labeled Dextran (MW 500 kDa) after transfer into the continuous water phase: (A) bright field image. (B) fluorescent image.

FIG. 5 shows dried Spider bags/balloons imaged by SEM. The membrane thickness has been determined to be smaller than 70 nm n.

FIG. 6 IR spectra in D₂O before (______.______.) and after (______ ) microcapsule formation. The shift in the spectra indicates a change in protein structure during microcapsule formation. Specifically, this shift indicates the formation of β-sheets. Deconvolution and Gaussian fit of microcapsule IR spectra reveals four peaks. Deconvoluted peaks are at 1621 cm⁻¹, 1642 cm⁻¹, 1661 cm⁻¹ and 1683 cm⁻¹ and are assigned respectively to β-sheets, random coil structures and two peaks for β-turns.

FIG. 7 Microcapsule permeability measurements. (A) Sample confocal image of a microcapsule in water with 0.3% 4 kDa FITC dextran added outside the microcapsule. A fraction of the dextran permeates the membrane. (B) Molecular weight distribution of dextran as measured by GPC fluorescence. (C) Measured molecular weight cutoff histogram for 51 microcapsules. Average molecular weight cutoff is 2.2 kDa.

FIG. 8 Proteinase K digestion of C₁₆ microcapsules. Top row phase contrast image. Bottom row fluorescent image. As indicated by loss of fluorescence, dextran is released shortly after Proteinase K addition. Complete digestion of microcapsules occurs after 13±1 minutes.

FIG. 9 Applied force versus microcapsule deformation as measured by AFM. Inset graph is the linear force regime during small deformations (ε<1%).

FIG. 10A and FIG. 10B illustrate the final steps in the synthesis of cyclic RGD molecules for use in the present invention.

EXAMPLES Protein Preparation

The protein solution, from which the spider balloons were formed, was prepared by first dissolving recombinant spider dragline silk protein (C₁₆, see Huemmerich et al., 2004) at a concentration of 10 mg/ml in 6M guanidine thiocyanate. The protein solution was cooled to 4° C. and the concentration of guanidine thiocyanate was reduced below 1 mM by dialyzing the protein solution against a 10 mM Tris buffer, pH 8.0 overnight using dialysis tubing from Carl Roth GmbH with a molecular weight cutoff of 14 kDa. Any undispersed protein was removed by centrifuging the dialyzed solution for 30 minutes at a force of 100.000 x g while maintaining the solution temperature at 4° C. The final protein concentration was determined using UV adsorption, employing the proteins extinction coefficient of 0.859 at a wavelength of 276 nm.

Microcapsule Formation

Microcapsules of spider silk were formed by emulsifying 5 μl of dialyzed protein suspension in 300 μl toluene for 90 seconds (FIG. 2A). During emulsification, silk protein adsorbs and changes its structural conformation at the surface of the emulsion droplets resulting in a polymer network that encapsulates the emulsion droplet (FIG. 2B). Spider silk microcapsules were formed using protein suspensions with concentrations ranging from 1 to 6 mg/ml and with emulsification times as short as 20 seconds. The size of the microcapsules formed depends on the size of the emulsion droplets.

Once formed, the protein shells surrounding the emulsion droplets were transferred from the two-phase emulsion into a one-phase solution. Two different methods are effective in transferring the protein shells. In the first method, 300 μl of water was added to the toluene to form an aqueous sublayer. The protein shells surrounding the water droplets were centrifuged from the toluene layer into the aqueous sublayer at a force of 100×g for 4 minutes (FIG. 2C). In the second method, a one-phase solution was formed by adding 300 μl of ethanol to the two-phase emulsion, in order to solubilize the toluene and water (FIG. 2D). After using either method to transfer the microcapsules to a one-phase solution, the resulting structures were investigated with an optical microscope (FIG. 3).

Unlike soluble C₁₆, whose structure is primarily random coil, the assembled protein has a β-sheet-rich conformation. The change in C₁₆ conformation upon assembly was observed using IR microscopy. Initially, C₁₆ solubilized in D₂O adsorbs at 1645 cm⁻¹, which is characteristic of proteins in a random coil structure (FIG. 6). After microcapsule formation two shoulders in the adsorption spectra emerge indicating a change in the secondary structure of C₁₆. Deconvolution of the spectra reveals the contribution of four Gaussian peaks at 1621 cm⁻¹, 1642 cm⁻¹, 1661 cm⁻¹ and 1683 cm¹.

The integrity of the centrifuged microcapsule-like protein shells was verified by adding 0.5 wt %, FITC labeled, 500 kDa Dextran (Sigma-Aldrich) to the protein solution prior to emulsification. After emulsification and centrifugation, the formed microcapsule-like structures continued to fluoresce indicating that the protein shell of these structures did not tear during centrifugation (FIG. 4). The microcapsule membrane can trap large molecules such as high molecular weight dextran but is permeable to small molecules such as fluorescein. If low molecular weight FITC labeled dextran is added to the outside of the centrifuged microcapsules a fraction of the dextran permeates the membranes and enters the capsules (FIG. 7A). The fractional admittance of the low molecular weight dextran occurs because the dextran has a non-finite polydispersity, comprising of both low and high dextran molecules (FIG. 7B). As a result the membrane admits the dextran below a certain molecular weight cutoff and excludes the dextran larger than this cutoff. By measuring the amount of fluorescence intensity inside the microcapsules and by using the fluorescent molecular weight distribution of the dextran (FIG. 7B) as measured by gel permeation chromatography, the molecular weight cutoff of the membrane was determined The permeability of 52 different microcapsules in 13 different samples were measured. The molecular weight cutoff of these microcapsules ranged from 0.3 kDa to 6.0 k-Da with an average molecular weight cutoff of 2.2 kDa (r_(g)˜18 Å) (FIG. 7C).

Enzymatic triggered release of contents, such as FITC-labeled dextran, was demonstrated using the enzyme Proteinase K (FIG. 8). As indicated by the loss of fluorescence, shortly after the addition of Proteinase K the integrity of the microcapsule membrane is destroyed and the dextran is released. After the release of the dextran, the enzyme continues to digest the microcapsule until complete digestion occurs at 13±1 minutes.

The enzymatic digestion of the microcapsules can be prevented by chemically cross-linking C₁₆ through photo-initiated oxidation with ammonium peroxodisufate (APS) and Tris (2,2′-bipyridyl) dichlororuthenium(II) (Rubpy). To chemically crosslink the C₁₆, 10 mM APS and 100 mM Rubpy are added to the centrifuged solution, and the reaction is photo-initiated by exposing the mixture to light from a tungsten lamp for 5 minutes. This cross-linking renders the C₁₆ microcapsules stable against treatment with Proteinase K. After cross-linking, the addition of 100 μM Proteinase K to the crosslinked microcapsules has no effect on capsule integrity even after incubation for one hour at 37° C. This behavior is markedly different from the non-crosslinked microcapsules which release the encapsulated dextran almost immediately under the same conditions.

The formed microcapsules are observed to be highly elastic. The elasticity of the microcapsules was measured by compression with an AFM. For the compression measurements a 35 micron glass sphere attached to an AFM cantilever with a spring constant of 10 pN/nm and force versus deformation curves were obtained for microcapsules with sizes ranging from 1 to 4 microns (FIG. 9). At small deformations the relationship between the applied force, f, and the resultant deformation, ε, is described by

f∝Eh ²ε/√{square root over (b 12(1−σ²))}

where h is the membrane thickness, E is the Young's modulus, σ is the Poisson ratio, and the pre-factor is a constant of an order of one. Using the maximum capsule wall thickness calculated from the initial concentration of silk monomer used and by assuming a Poisson ratio of 0.5, the microcapsules were determined to have a Young's modulus between E=0.7-3.6 GPa. The capsules also demonstrate excellent chemical stability. The addition of protein denaturants such as 2% sodium dodecylsulfate (SDS) and 8M urea has no effect on capsule integrity. The microcapsules were observed to be stable under these conditions for weeks.

REFERENCES

-   Chécot F, Lecommandoux S, Gnanou Y, Klok H A (2002) Angew. Chem.     Int. Ed. 41, 1339 -   Chécot F, Lecommandoux S, Klok H A, Gnanou Y (2003) Euro. Phys. J. E     10, 25 -   Dinsmore A D, Hsu M F, Nikolaides M G, Marquez M, Bausch A R, Weitz     D A. (2002) Colloidosomes: Selectively permeable capsules composed     of colloidal particles. Science 298(5595):1006-1009 -   Y. Y. Won, H. Davis, F. Bates, Science 283, 960 (1999) -   Huemmerich D, Helsen C W, Quedzueweit S, Oschmann J, Rudolph R,     Scheibel T (2004) Primary structure elements of spider dragline     silks and their contribution to protein solubility. Biochemistry 43:     13604-12 -   Scheibel T (2004) Spider silks: recombinant synthesis, assembly,     spinning, and engineering of synthetic proteins, Microbial Cell     Factories 3, 14 

What is claimed is:
 1. A nanocapsule of spider silk proteins, wherein the spider silk proteins form a polymer network that encapsulates an emulsion droplet.
 2. The nanocapsule of spider silk proteins of claim 1, wherein said nanocapsule has a wall.
 3. The nanocapsule of spider silk proteins of claim 2, wherein the wall thickness of said nanocapsule is between 5 and 100 nm.
 4. The nanocapsule of spider silk proteins of claim 1, wherein the spider silk proteins comprise 5 to 50 repeat units, wherein the repeat unit is selected from the group consisting of the amino acid sequence according to SEQ ID NO: 3, the amino acid sequence according to SEQ ID NO: 4, and the amino acid sequence according to SEQ ID NO:
 5. 5. The nanocapsule of spider silk proteins of claim 1, wherein the spider silk proteins are selected from the group consisting of C₁₆, C₃₂, (AQ)₁₂, (AQ)₂₄, (QAQ)₈ and (QAQ)₁₆, wherein C represents the amino acid sequence according to SEQ ID NO: 5, A represents the amino acid sequence according to SEQ ID NO: 3 and Q represents the amino acid sequence according to SEQ ID NO:
 4. 6. The nanocapsule of spider silk proteins of claim 1, wherein the nanocapsule comprises pharmaceutical agents, cosmetical agents, foodstuffs or food additives.
 7. The nanocapsule of spider silk proteins of claim 6, wherein the pharmaceutical agents, cosmetical agents, foodstuffs or food additives are encapsulated in the nanocapsule.
 8. The nanocapsule of spider silk proteins of claim 6, wherein the nanocapsule is coated by the pharmaceutical agents, cosmetical agents, foodstuffs or food additives.
 9. A microcapsule of spider silk proteins, wherein the spider silk proteins form a polymer network that encapsulates an emulsion droplet.
 10. The microcapsule of spider silk proteins of claim 9, wherein said microcapsule has a wall.
 11. The microcapsule of spider silk proteins of claim 10, wherein the wall thickness of said microcapsule is between 5 and 100 nm.
 12. The microcapsule of spider silk proteins of claim 9, wherein the spider silk proteins comprise 5 to 50 repeat units, wherein the repeat unit is selected from the group consisting of the amino acid sequence according to SEQ ID NO: 3, the amino acid sequence according to SEQ ID NO: 4 and the amino acid sequence according to SEQ ID NO:
 5. 13. The microcapsule of spider silk proteins of claim 9, wherein the spider silk proteins are selected from the group consisting of C₁₆, C₃₂, (AQ)₁₂, (AQ)₂₄, (QAQ)₈ and (QAQ)₁₆, wherein C represents the amino acid sequence according to SEQ ID NO: 5, A represents the amino acid sequence according to SEQ ID NO: 3 and Q represents the amino acid sequence according to SEQ ID NO:
 4. 14. The microcapsule of spider silk proteins of claim 9, wherein said microcapsule comprises pharmaceutical agents, cosmetical agents, foodstuffs or food additives.
 15. The microcapsule of spider silk proteins of claim 14, wherein the pharmaceutical agents, cosmetical agents, foodstuffs or food additives are encapsulated in the microcapsule.
 16. The nanocapsule of spider silk proteins of claim 14, wherein the microcapsule is coated by the pharmaceutical agents, cosmetical agents, foodstuffs or food additives.
 17. A pharmaceutical composition containing the nanocapsule of claim 1 and a pharmaceutically acceptable carrier.
 18. A pharmaceutical composition containing the microcapsule of claim 9 and a pharmaceutically acceptable carrier.
 19. A cosmetical or food product containing the nanocapsule of claim
 1. 20. A cosmetical or food product containing the microcapsule of claim
 9. 